In Vitro Mineralization Assay

To test the ability of engineered BL21(DE3) E. coli strain to precipitate CaCO3, we performed an in vitro mineralisation assay, adapting Zhu, et al. 's technique. Bacteria were cultured overnight in 30mL of LB +Kanamycin medium and 0.5 mM ZnSO4 at 25℃. IPTG induction was performed 3 hours prior to experimentation. The assay was run on 8 mL Tris-HCl buffer 8.3 and 50mL of saturated CO2 aqueous solution at 0℃. 3 mL of cell pellet were introduced into the solution, and the reaction was allowed to proceed on ice for an hour. At this point, the bacteria should have been able to produce bicarbonate ions. Cells were removed from the solution by centrifugation (15 min x 5000g). 25mL of a 0.3M solution of CaCl2 was added to the remaining supernatant as a calcium source. The reaction was left to run at 25℃ for 12h. Samples were filtered using vacuum filtration and dried at 50℃ to evaporate the solvent. Solid mass was weighed and recorded as “Wet Weight”. Upon preliminary analysis of FT-IR data, it was concluded that the mineral sample contained a large amount of water, elucidated by the stretching O-H peak at 3400 cm.1. Hence, the sample was dried further in liquid nitrogen for 48 hours, final weight was recorded at 2.3 g (yield=306.17%). Precipitated dry crystals were analysed using ATR-IR and 3C NMR

User Reviews

UNIQ960bc1aea507204f-partinfo-00000000-QINU UNIQ960bc1aea507204f-partinfo-00000001-QINU