Difference between revisions of "Part:BBa K643000"

Revision as of 23:33, 9 October 2011

CDS7 cadmium sulfate binding peptide coding sequence

The protein coded by this part is claimed to be capable of binding to cadmium chloride and sodium sulfide, forming a cadmium sulfate nanocrystal that exhibits quantum dot behavior.

Experience

Four experiments were run testing the CDS7 biobrick part in the expression plasmid pET28b. The Nco1 and BamH1 sites engineered into the part were used to clone it into the multiple cloning site of pET28b under the control of an IPTG-inducible promotor. A consensus quantum dot synthesis protocol from the literature was used. E. coli strain Jm109 transformed with the pET28b/CDS7 plasmid was tested against JM109 transformed with pET28b with no insert. Cells were inoculated at OD600 = 0.1 and grown to log phase (OD600=0.5) at which time IPTG was added to induce the synthesis of CDS7. In the first experiment CdCl2 was added (either 1mM or 10mM)at the same time as IPTG and the cells incubated with shaking for an additional 3h at 37C. In the second experiment the cells were treated with IPTG as above, abut allowed to incubate for 2h before the CdCl2 was added and then allowed to grow for 3h. In both cases the 3h incubation was followed by removal of the cells from the 37C shaker. Sodium sulfide (Na2S) was added and the cells rotated end-over-end at room temperature for 1.5hr. They were then washed 4x with distilled water and analyzed with fluorescence microscopy. Samples were pET28b/CDS7, pET28b, no cells. All samples were tested +/- CdCl2 and +/- Na2S. In a third experiment, the conditions were the same as the second above except an arm with +/-IPTG was added.

In a fourth experiment ZnCl2 (10mM) was used in place of CdCl2, using the conditions in the third experiment.

Result

quantumdot

Picture from the first experiment described above, sample was E. coli JM109 cells transformed with pET28b/CDS7 plasmid, induced with IPTG and treated with 10mM CdCl2 and sodium sulfide as described above. Cells exhibit fluorescent behavior from green to red but negative controls exposed to cadmium and sulfide mixture without engineered genetic sequence showed similar, possibly little less, amount of fluorescence by eye.

Image 2

The presence of large clumps of flocculent orange precipitate prevented us from using flow cytometry or fluorimetry to analyze the samples for fluorescence intensity.

Future

We plan to carry on the experiment even after the iGEM and complete quantum dot producing system for future iGEM projects